ZORTRAX FILAMENTS
We provide all
Zortrax M200 materials which are available to buy online. Z-ULTRAT is a
stronger and more durable option which has a semi matt finish. Z-ABS
which is the economical choice available in many different colours and has a
matt finish. Z-HIPS is the material with a high impact resistance and is also
resistant to solvents. There is a stunning looking glass fibre blend called
Z-GLASS which is semi transparent and has very low shrinkage. Z-PETG is a
material that is highly resistant to salts, acids and alkalis. Z-PCABS is a
high strength material that is also resistant to high and low
temperatures. All the Zortrax materials have been specially formulation
for the Zortrax M200 3D printers.
We provide all
the Zortrax M300 filaments which are available to buy online. Z-HIPS is
the material with a high impact resistance and is also resistant to solvents.
There is a stunning looking glass fibre blend called Z-GLASS which is semi
transparent and has very low shrinkage. Z-PETG is a material that is highly
resistant to salts, acids and alkalis. Z-ASA Pro is UV stable and weather
resistant. Z-ESD is for parts that require electrostatic discharge protection.
All the Zortrax M300 materials
have been specially formulated for the Zortrax M300 3D printers
You can supply Zortrax items through Ziel-Tech
Zortrax Filaments
Z-ABS
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax M200
|
spool
|
800 g ±5%
|
1.75 mm
|
Single
|
|
Zortrax M200 Plus
|
|
Zortrax Inventure
|
|
Zortrax M300 Plus
|
2000 g ±5%
|
|
Zortrax M300 Dual
|
Single / Dual with Z-SUPPORT ATP
|
|
Key Properties of
Z-ABS
|
Metric
|
Imperial
|
Test Method
|
|
Izod Impact, Notched
|
8.93 kJ/m2
|
4.25 ft-lb/in2
|
ISO 180:2004
|
|
Elongation at Break
|
11.08%
|
11.08%
|
ISO 527:1998
|
|
Glass Transition
Temperature
|
107.89° C
|
226° F
|
ISO 11357-3:2014
|
Z-ABS 2
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax M200
|
spool
|
800 g ±5%
|
1.75 mm
|
Single
|
|
Zortrax M200 Plus
|
|
Zortrax M300 Plus
|
|
Key Properties of
Z-ABS 2
|
Metric
|
Imperial
|
Test Method
|
|
Izod Impact, Notched
|
9 kJ/m2
|
4.28 ft-lb/in2
|
ISO 180/A
|
|
Tensile Elongation
|
2.5%
|
2.5%
|
ISO 527-2
|
|
Vicat Softening
Temperature
|
97° C
|
207° F
|
ISO 306/B50
|
Z-ASA Pro
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax M200
|
spool
|
800 g ±5%
|
1.75 mm
|
Single
|
|
Zortrax M200 Plus
|
|
Zortrax Inventure
|
|
Zortrax M300
|
2000 g ±5%
|
|
Zortrax M300 Plus
|
|
Zortrax M300 Dual
|
Single / Dual with Z-SUPPORT ATP
|
|
Key Properties
|
Metric
|
Imperial
|
Test Method
|
|
Izod Impact, Notched
|
3.81 kJ/m2
|
1.81 ft-lb/in2
|
ISO 180:2004
|
|
Flexural Modulus
|
1.36 GPa
|
197 ksi
|
ISO 178:2011
|
|
Glass Transition
Temperature
|
80.99° C
|
178° F
|
ISO 11357-3:2014
|
Z-ESD
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax M200
|
spool
|
800 g ±5%
|
1.75 mm
|
Single
|
|
Zortrax M200 Plus
|
|
Zortrax Inventure
|
Single / Dual with Z-SUPPORT PREMIUM
|
|
Zortrax M300
|
2000 g ±5%
|
Single
|
|
Zortrax M300 Plus
|
|
Zortrax M300 Dual
|
Dual with Z-SUPPORT PREMIUM
|
|
Key Properties of
Z-ESD
|
Metric
|
Imperial
|
Test Method
|
|
Tensile Strength
|
32.88 MPa
|
4770 psi
|
ISO 527:1998
|
|
Flexural Modulus
|
1.50 GPa
|
218 ksi
|
ISO 178:2011
|
|
Glass Transition
Temperature
|
79.93° C
|
176° F
|
ISO 11357-3:2014
|
|
|
Key Properties of
Z-ESD v2
|
Metric
|
Imperial
|
Test Method
|
|
Tensile Modulus
|
2.3 - 2.4 GPa
|
334 - 348 ksi
|
DIN 53457
|
|
Glass Transition
Temperature
|
80 - 90° C
|
176 - 194° F
|
DSC
|
Z-FLEX
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax M200 Plus
|
spool
|
800 g ± 5%
|
1.75 mm
|
Single
|
|
Zortrax M300 Plus
|
|
Zortrax Inventure
|
|
Zortrax M300 Dual
|
|
Key Properties
|
Metric
|
Imperial
|
Test Method
|
|
Shore Hardness
|
31D
|
31D
|
ISO 868:1998
|
|
Elongation at Break
|
3319.12%
|
3319.12%
|
ISO 527:1998
|
|
Resistance to
Surface Abrasion
|
95 mg
|
1.46 gr
|
D1044 (wheel H-18)
|
Z-GLASS
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax M200
|
spool
|
800 g ±5%
|
1.75 mm
|
Single
|
|
Zortrax M200 Plus
|
|
Zortrax Inventure
|
Single / Dual with Z-SUPPORT Premium
|
|
Zortrax M300
|
2000 g ±5%
|
Single
|
|
Zortrax M300 Plus
|
|
Zortrax M300 Dual
|
Single / Dual with Z-SUPPORT Premium
|
|
Key Properties
|
Metric
|
Imperial
|
Test Method
|
|
Tensile Strength
|
39.57 MPa
|
5740 psi
|
ISO 527:1998
|
|
Elongation at max
Tensile Stress
|
5.94%
|
5.94%
|
ISO 527:1998
|
|
Glass Transition
Temperature
|
78.06° C
|
173° F
|
ISO 11357-3:2014
|
Z-HIPS
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax M200
|
spool
|
800 g ±5%
|
1.75 mm
|
Single
|
|
Zortrax M200 Plus
|
|
Zortrax M300
|
2000 g ±5%
|
|
Zortrax M300 Plus
|
|
Zortrax M300 Dual
|
|
Key Properties
|
Metric
|
Imperial
|
Test Method
|
|
Elongation at Break
|
7.75%
|
7.75%
|
ISO 527:1998
|
|
Shore Hardness (D)
|
73.2
|
73.2
|
ISO 868:1998
|
|
Glass Transition
Temperature
|
98.68° C
|
210° F
|
ISO 11357-3:2014
|
Z-NYLON
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax M200 Plus
|
spool
|
800 g ± 5%
|
1.75 mm
|
Single
|
|
Zortrax Inventure
|
|
Zortrax M300 Plus
|
2000 g ± 5%
|
|
Zortrax M300 Dual
|
|
Key Properties
|
Metric
|
Imperial
|
Test Method
|
|
Flexural Modulus
|
781.01 MPa
|
113 ksi
|
ISO 178:2011
|
|
Tensile Strength
|
33.22 MPa
|
4820 psi
|
ISO 527:1998
|
|
Melting Point
|
172.81° C
|
343° F
|
ISO 11357-3:2014
|
Z-PCABS
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax M200
|
spool
|
800 g ±5%
|
1.75 mm
|
Single
|
|
Zortrax M200 Plus
|
|
Zortrax M300 Plus
|
|
Key Properties
|
Metric
|
Imperial
|
Test Method
|
|
Izod Impact, Notched
|
11.40 kJ/m2
|
5.42 ft-lb/in2
|
ISO 180:2004
|
|
Glass Transition
Temperature
|
104.1° C
|
219° F
|
ISO 11357-3:2014
|
|
Shore Hardness (D)
|
73.0
|
73.0
|
ISO 868:1998
|
Z-PEEK
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax Endureal
|
spool
|
1000 g ±5%
|
1.75 mm
|
Dual with Z-SUPPORT High-Temp
|
|
Key Properties
|
Metric
|
Imperial
|
Test Method
|
|
Tensile Modulus
|
3720 MPa
|
540 ksi
|
ISO 527
|
|
Tensile Elongation
|
28%
|
28%
|
ISO 527
|
|
Flexural Modulus
|
2700 MPa
|
392 ksi
|
ISO 178
|
|
Outgassing
Properties
|
|
Property
|
Value
|
Standard
|
|
TML (%)
|
0.31
|
ECSS-Q-ST-70-02C
|
|
CVCM (%)
|
0.000
|
ECSS-Q-ST-70-02C
|
|
RML (%)
|
0.14
|
ECSS-Q-ST-70-02C
|
Z-PEI 1010
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax Endureal
|
spool
|
1000 g ±5%
|
1.75 mm
|
Dual with Z-SUPPORT High-Temp
|
|
Key Properties
|
Metric
|
Imperial
|
Test Method
|
|
Tensile Strength
|
56 MPa
|
8120 psi
|
ISO 527
|
|
Flexural Modulus
|
2510 MPa
|
364 ksi
|
ISO 178
|
|
Glass Transition
Temperature
|
217 °C
|
423° F
|
DSC
|
Z-PEI 9085
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax Endureal
|
spool
|
1000 g ±5%
|
1.75 mm
|
Single / Dual with Z-SUPPORT High-Temp
|
|
Key Properties
|
Metric
|
Imperial
|
Test Method
|
|
Tensile Strength
|
54 MPa
|
7830 psi
|
ISO 527
|
|
Flexural Modulus
|
2170 MPa
|
315 ksi
|
ISO 178
|
|
Glass Transition
Temperature
|
186 °C
|
367 °F
|
DSC
|
Z-PETG
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax Inventure
|
cartridge
|
350 g ±5%
|
1.75 mm
|
Single / Dual with Z-SUPPORT Premium
|
|
Zortrax M200
|
spool
|
800 g ±5%
|
Single
|
|
Zortrax Inventure
|
Single / Dual with Z-SUPPORT Premium
|
|
Zortrax M200 Plus
|
Single
|
|
Zortrax M300
|
2000 g ±5%
|
|
Zortrax M300 Plus
|
|
Zortrax M300 Dual
|
Single / Dual with Z-SUPPORT Premium
|
|
Key Properties
|
Metric
|
Imperial
|
Test Method
|
|
Izod Impact, Notched
|
3.27 kJ/m2
|
1.56 ft-lb/in2
|
ISO 180:2004
|
|
Elongation at max
Tensile Stress
|
6.39%
|
6.39%
|
ISO 527:1998
|
|
Glass Transition
Temperature
|
77.65° C
|
172° F
|
ISO 11357-3:2014
|
Z-PLA
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax Inventure
|
cartridge
|
350 g ±5%
|
1.75 mm
|
Single / Dual with Z-SUPPORT Premium
|
|
Zortrax Inventure
|
spool
|
800 g ±5%
|
|
Zortrax M200 Plus
|
Single
|
|
Zortrax M300 Plus
|
2000 g ±5%
|
|
Zortrax M300 Dual
|
Single / Dual with Z-SUPPORT Premium
|
|
Key Properties
|
Metric
|
Imperial
|
Test Method
|
|
Tensile Strength
|
47.95 MPa
|
6950 psi
|
ISO 527:1998
|
|
Bending Stress
|
56.80 MPa
|
8240 psi
|
ISO 178:2011
|
|
Glass Transition
Temperature
|
57.06° C
|
135° F
|
ISO 11357-3:2014
|
Z-PLA Pro
|
edicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax M200
|
spool
|
800 g ±5%
|
1.75 mm
|
Single
|
|
Zortrax M200 Plus
|
|
Zortrax Inventure
|
Single / Dual with Z-SUPPORT Premium
|
|
Zortrax M300
|
2000 g ±5%
|
Single
|
|
Zortrax M300 Plus
|
|
Zortrax M300 Dual
|
Single / Dual with Z-SUPPORT Premium
|
|
Key Properties
|
Metric
|
Imperial
|
Test Method
|
|
Bending Stress
|
58.60 MPa
|
8500 psi
|
ISO 178:2011
|
|
Shore Hardness (D)
|
77.6
|
77.6
|
ISO 868:1998
|
|
Glass Transition
Temperature
|
48.82° C
|
120° F
|
ISO 11357-3:2014
|
Z-SEMIFLEX
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax M200 Plus
|
spool
|
800 g ±5%
|
1.75 mm
|
Single
|
|
Zortrax M300 Plus
|
2000 g ±5%
|
|
Key Properties
|
Metric
|
Imperial
|
Test Method
|
|
Izod Impact, Notched
|
38.88 kJ/m2
|
18.5 ft-lb/in2
|
ISO 180:2004
|
|
Elongation at max
Tensile Stress
|
524%
|
524%
|
ISO 527:1998
|
|
Melting point
|
180.16° C
|
356° F
|
ISO 11357-3:2014
|
Z-SUPPORT ATP
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
|
Zortrax Endureal
|
spool
|
750 g ±5%
|
1.75 mm
|
|
Zortrax M300 Dual
|
|
Support material
compatible with
|
|
Z-ABS, Z-ASA Pro,
Z-ESD, Z-ULTRAT, Z-ULTRAT Plus
|
|
|
|
Z-SUPPORT ATP 130
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
|
Zortrax Endureal
|
spool
|
750 g ±5%
|
1.75 mm
|
|
Support material
compatible with
|
|
Z-PEEK, Z-ULTRAT
Plus
|
|
|
|
Z-SUPPORT High-Temp
|
edicated for
|
Container
|
Weight
|
Diameter
|
|
Zortrax Endureal
|
spool
|
1000 g ±5%
|
1.75 mm
|
|
|
|
|
Support material
compatible with
|
|
Z-PEEK, Z-PEI 1010,
Z-PEI 9085
|
|
|
|
Z-SUPPORT Premium
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
|
Zortrax Inventure
|
cartridge
|
350 g ±5%
|
1.75 mm
|
|
spool
|
350 g ±5%
|
|
Zortrax M300 Dual
|
spool
|
800 g ±5%
|
|
Support material
compatible with
|
|
Z-GLASS, Z-PETG,
Z-PLA, Z-PLA Pro, and Z-ULTRAT Plus
|
Z-ULTRAT
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax M200
|
spool
|
800 g ±5%
|
1.75 mm
|
Single
|
|
Zortrax M200 Plus
|
|
Zortrax Inventure
|
|
Zortrax M300
|
2000 g ±5%
|
|
Zortrax M300 Plus
|
|
Zortrax M300 Dual
|
Single / Dual with Z-SUPPORT ATP
|
|
Key Properties
|
Metric
|
Imperial
|
Test Method
|
|
Flexural Modulus
|
1.85 GPa
|
268 ksi
|
ISO 178:2011
|
|
Shore Hardness (D)
|
73.4
|
73.4
|
ISO 868:1998
|
|
Glass Transition
Temperature
|
106.40° C
|
224° F
|
ISO 11357-3:2014
|
Z-ULTRAT Plus
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax Inventure
|
cartridge
|
350 g ±5%
|
1.75 mm
|
Single / Dual with Z-SUPPORT Premium
|
|
Zortrax M300 Dual
|
spool
|
2000 g ±5%
|
Single / Dual with Z-SUPPORT Premium or Z-SUPPORT ATP
|
|
Zortrax Endureal
|
Single
|
|
Key Properties
|
Metric
|
Imperial
|
Test Method
|
|
Flexural Modulus
|
1.51 GPa
|
219 ksi
|
ISO 178:2011
|
|
Breaking Stress
|
31.32 MPa
|
4540 psi
|
ISO 527:1998
|
|
Glass Transition
Temperature
|
70.19° C
|
158° F
|
ISO 11357-3:2014
|
BASF Ultrafuse® PAHT CF15
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax M300 Dual
|
spool
|
750 g ± 5%
|
1.75 mm
|
Single / Dual with Z-SUPPORT ATP
|
|
Key Properties
|
Metric
|
Imperial
|
Test Method
|
|
Young’s Modulus
|
8386 MPa
|
1216 ksi
|
ISO 527
|
|
Elongation at Break
|
1.8 %
|
1.8 %
|
ISO 527
|
|
HDT at 0.45 MPa
|
145 °C
|
293 °F
|
ISO 75-2
|
BASF Ultrafuse® PP GF30
|
Dedicated for
|
Container
|
Weight
|
Diameter
|
Extrusion
|
|
Zortrax M300 Dual
|
spool
|
700 g ± 5%
|
1.75 mm
|
Single
|
|
|
Key Properties
|
Metric
|
Imperial
|
Test Method
|
|
Flexural Modulus
|
3507 MPa
|
509 ksi
|
ISO 178
|
|
Tensile Strength
|
41.7 MPa
|
6.0 ksi
|
ISO 527
|